Description
BHARATCOL P-180 Adhesiveis room temperature curing adhesive with syrupy consistency. It is water soluble PVA based resin. The material does not contain by recipe substances listed in Restriction of Hazardous Substances (RoHS) Directive (2002/95/EC).
Areas of Application
As an insulating adhesive it can be usedin construction of oil filled power and distribution transformers. BHARATCOL P-180 Adhesive is also recommended for gluing cotton tape, hand boards, laminated wood, and similar fibrous materials.
Properties of cured material
The cured film of BHARATCOL P-180 is resistant to transformer oil andchlorinated diphenyl.
Application Methods
BHARATCOL P-180 can be applied by brush or spatula. Viscosity of BHARATCOL P-180 Adhesive can be reduced by addition of distilled water depending upon the desired application.
Properties of BHARATCOL P-180 Adhesive as supplied
| Colour and appearance [*] | DBI 1001 [**] | Off white, Clear tohazy | |
| Solids content [*] | DBI 1022 [**] 1.5 g/105°C/2 h | % | 19 -21 |
| Viscosity at 23°C [*] | DBI 3005 [**] By Brookfield | mpa.s | 10000 – 15000 |
| Density at 23°C | ISO 1675 | g/ml | NA |
| Flash point by closed cup | DBI 1001 [**] | NA | |
| Recommended Thinner | Distilled water | ||
| Compatibility with distilled water [*] | DBI 1006 [**] | – | – |
| Storage life [*] | When stored in original sealed container at RT | months | 12 |
[*] These properties form our sales specification
[**] DBI are internal test methods and are available on request
Recommended Curing Cycle :
4- 8 at room temperature
To obtain good dielectric properties and resistance to transformer oil and chlorinated diphenyl it is necessary to post cure BHARATCOL P-180 Adhesive for 2-4 h at 100-1100Cand/or dry it under vacuum.
The suggested curing time is after the unit attains the specified temperature.
Cured Film Properties:
| Drying in a thin film | DBI 3031 [**] | 1 h at 120°C | NA |
| Curing in a thick layer | DBI 3007 [**] 0 20 g / 120 C / 4 h | Top, Bottom, Inside | NA |
| Resoftening | IS 10026 | at 120°C | NA |
| Bond Strength | IEC 61033 | at RT | NA |
| At 130°C | NA |
Temperature Index :
| IEC 60216 by weight loss measurement | 30% weight loss | °C |
Dielectric Properties Specimen Curing -
| Dielectric strength as per IEC 60455-2 | at R.T. after 24 h water immersion at RT | kV/mm | NA |
| Volume resistivity at 500 V DC as per IEC 60455-2 | at R.T. after 168 h water immersion at R.T. | ohm.cm | NA |
| Dielectric constant at 30 V/1 kHz as per IEC 60455-2 | at R.T. at 130°C | – | NA |
| Dielectric loss factor 30 V/1 kHz as per IEC 60455-2 | at R.T. at 130°C | – | NA |
| Adhesive strength on wood pieces | At R.T | N/mm2 | 4 |
Resistance against solvents & chemicals
| Solvent resistance as per | 10% H2SO4 | No Change in colour | – |
| IEC 60455-2 | 2% NaOH | No Change in colour | – |
Packaging
1 and 30 kg in polyethylene containers.
Safe Handling
BHARATCOL P-180 Adhesiveis a flammable liquid. Use foam, CO2 or dry chemical powder for fire fighting. Inhalation and direct contact with the skin should be avoided. In case of contact, the affected area should be washed with soap and plenty of water. For further details ask for our material safety data sheet 2-15.
Desclaimer
This information is intended only for general guidance in the application of our product. It has been obtained by careful investigation and represents the present state of our knowledge and experience.Because of the large number of possible methods of application and processing we are not able to assume responsibility inany one particular case for either the technical results or the patent rights situation applicable to the country under consideration.